Centrifugal casting technology

Centrifugal casting or rotocasting is a casting technique that is typically used to cast thin-walled cylinders. It is used to cast steel, copper and others. It is noted for the high quality of the results attainable, particularly for precise control of their metallurgy and crystal structure.

The centrifugal casting products BACSOONT are manufacturing include centrifugal casting copper bushing, centrifugal high manganese steel bushing, centrifugal casting steel bushing, centrifugal casting steel pipe and others, the OD can meet dimensions of 20 mm to 2000 mm.

Material information:

  • Steel
    Material C Si Mn P S Cr Mo Ni W
    ZG120Mn7Mo1 1.05 ~ 1.35 0.3 ~ 0.9 11 ~ 14 ≤0.060 ≤0.040 0.9 ~ 1.2
    ZG110Mn13Mo1 0.75 ~ 1.35 0.3 ~ 0.9 11 ~ 14 ≤0.060 ≤0.040 0.9 ~ 1.2
    ZG110Mn13 0.90 ~ 1.05 0.3 ~ 0.9 11 ~ 14 ≤0.060 ≤0.040
    ZG120Mn13 1.05 ~ 1.35 0.3 ~ 0.9 11 ~ 14 ≤0.060 ≤0.040
    ZG120Mn13Cr2 1.05 ~ 1.35 0.3 ~ 0.9 11 ~ 14 ≤0.060 ≤0.040 1.5 ~ 2.5
    ZG120Mn13W1 1.05 ~ 1.35 0.3 ~ 0.9 11 ~ 14 ≤0.060 ≤0.040 0.9 ~ 1.2
    ZG120Mn13Ni3 1.05 ~ 1.35 0.3 ~ 0.9 11 ~ 14 ≤0.060 ≤0.040 3.0 ~ 4.0
    ZG90Mn14Mo1 0.70 ~ 1.00 0.3 ~ 0.6 13 ~ 15 ≤0.070 ≤0.040 1.0 ~ 1.8
    ZG120Mn17 1.05 ~ 1.35 0.3 ~ 0.9 16 ~ 19 ≤0.060 ≤0.040
    ZG120Mn17Cr2 1.05 ~ 1.35 0.3 ~ 0.9 16 ~ 19 ≤0.060 ≤0.040 1.5 ~ 2.5
    Material C Mn Si Cr Ni Mo S P
    GB ZG120Mn13 1.05 ~ 1.35 11.00 ~ 14.00 0.3 ~ 0.9  ~  ~  ~ ≤0.040 ≤0.060
    AISI/SAE J91109 1.05 ~ 1.35 11.5 ~ 14.00 ≤1.00  ~  ~  ~ ≤0.050 ≤0.070
    JIS SCMnH1 0.90 ~ 1.30 11.00 ~ 14.00  ~  ~  ~  ~ ≤0.040 ≤0.1
    ГОСТ 110г13л 0.90 ~ 1.5 11.5 ~ 15.0 0.30 ~ 1.00 ≤1.00 ≤1.00  ~ ≤0.050 ≤0.120
    DIN GX120Mn13 1.05 ~ 1.35 11.00 ~ 14.00 0.3 ~ 0.9  ~  ~  ~ ≤0.045 ≤0.060
  • Bronze/Copper
    Material grade
    (GB)
    Main features Applications
    ZCuPb10Sn10 Lubrication performance, wear resistance and corrosion resistant performance is good, suitable for bimetal casting materials Surface pressure is high, and there is the lateral pressure of the sliding bearing, such as rolling rolling, vehicle use bearing, load peaks 60 mpa hit parts, as well as the highest peak of 100 mpa bimetallic bearing bush of the internal combustion engine, and the piston pin sets, lining, etc.
    ZCuPb15Sn8 Under the condition of lack of lubricant and use water quality lubricants, sliding and lubricating, free cutting, casting performance is poor, for dilute sulfuric acid corrosion resistant performance is good Surface pressure is high, and the lateral pressure of bearing, copper cooling pipe can be made from cold rolling mill, impact resistance load of up to 50 mpa parts, internal combustion engines of bimetallic bearing, mainly used for the biggest load of 70 mpa of piston pin set, acid-proof accessories
    ZCuPb20Sn5 At higher sliding performance, in the absence of a lubricating medium and water as medium are particularly good self-lubricating performance suitable for bimetal casting material, sulfuric acid corrosion resistance, easy cutting, casting performance is poor High sliding speed of the bearing, and crusher, water pump, cold rolling mill bearings, piston pin load of 70 mpa
    ZCuPb30 Have good self-lubrication, free cutting, casting performance is poor, easy to produce the gravity segregation High sliding velocity of bimetallic bearing shell, wearing parts, etc.
    ZCuZn25Al6Fe3Mn3 With high mechanical properties, the casting performance is good, good corrosion resistance, has a tendency to stress corrosion Suitable for high strength, wear parts, such as bridge plate, nut, screw, wear-resistant plate, the slider, and worm gear, etc
    ZCuZn26Al4Fe3Mn3 With high mechanical properties, the casting performance is good, in the air, water, and seawater corrosion resistance is good, can be welded Require high strength, corrosion resistant parts
    ZCuZn38Mn2Pb2 Have higher mechanical properties and good corrosion resistance, abrasion resistance, good cutting performance General purpose structure, ship, instrument appearance, simple casting using such as sleeve, sleeve, bearings, slider, etc
    ZCuZn40Mn3Fe1 With high mechanical properties, good casting properties and machinability, and in the air, water, and water has good corrosion resistance, has a tendency to stress corrosion cracking Seawater corrosion parts, pipe fittings and under 300 °C, manufacturing and other large Marine propeller castings
    ZCuZn33Pb2 Structural material, feed temperature is 90 °C when good oxidation resistance, electrical conductivity of about 10 ~ 14 ms/m The shell of gas and water supply equipment, machinery manufacturing, electronics, precision instruments and optical instruments of component parts
    Other standard and material ASTM, JIS, AISI, EN, BS;
    Manganese brass: C86300 and etc.;
    Tin bronze: C83600, C93200, CuSn12, CuSn7Zn4Pb7 and etc.;
    Aluminum Bronze: C62900, C95400, C95500, CuAl10Fe5Ni5 and etc..

BACSOONT’s feature:

  • Centrifugal casting high manganese steel bushing (Eccentric and Concentric)
    OD’s dimensions of 50 mm to 400 mm
  • Centrifugal casting copper/bronze bushing (Concentric)
    OD’s dimensions of 20 mm to 2000 mm
  • Material: high manganese steel, copper, bronze
  • Heat treatment
  • Rapid water quench
  • CNC machining

Some products
centrifugal casting copper bushing-Bacsoont
centrifugal casting steel bushing-Bacsoont
centrifugal casting casting steel bushing-Bacsoont
centrifugal casting high manganese steel eccentric bushing-Bacsoont
copper bushing-Bacsoont